TYPISCH NORMEN
| GRAAD | MATEN ROUTINEMATIG GEVULD | ||
|---|---|---|---|
| Humeur | Dikte (Metrisch% 2fImperial) | Breedte | Lengte |
| 3105-O | Informeer voor maten | ||
| 3105-H22 | Informeer voor maten | ||
| 3105-H24 | Informeer voor maten | ||
| 3105-H26 | Informeer voor maten | ||
| 3105-H28 | Informeer voor maten |
ALGEMEEN INFO OVER 3105 ALUMINIUM BLAD
3105 aluminum sheet is 98 percent pure aluminum with the addition of specific alloys for strength improvement. This alloy can't be hardened by heat treatment. It has excellent weldability, formability, and corrosion resistance.
MEER DETAILS OVER 3105 ALUMINIUM BLAD
VOORDELEN/NADELEN INDUSTRIEËN BEWERKING WARMTE BEHANDELING
Voordelen/Nadelen
Het heeft uitstekend corrosie weerstand en vervormbaarheid. Aan de andere hand% 2c het is niet warmtebehandelbaar.
CHEMISCHE EIGENSCHAPPEN
| SI | FE | CU | MN | MG | CR | ZN | TI |
|---|---|---|---|---|---|---|---|
| 0.60 procent | 0.70 procent | 0.30 procent | 0.30-0.80 percent | 0.20-0.80 percent | 0.20 procent | 0.40 procent | 0.10 procent |
| VERLENGING | |||
|---|---|---|---|
| Ultiem Treksnelheid Sterkte (min - max) | Ultiem Opbrengst Sterkte | procent at 50mm | |
| 3105-O | 110-155 MPa / 15,194 - 22,480 psi | - | 16 |
| 3105-H12 | 130-175 MPa / 18,854 - 25,381 psi | 115 MPa / 16,679 psi | 2 |
| 3105-H14 | 160-205 MPa / 23,206 - 29,732 psi | 145 MPa % 2f 21% 2c030 psi | 2 |
| 3105-H16 | 185-230 MPa / 26,831 - 33,358 psi | 170 MPa / 24,656 psi | 1 |
| 3105-H18 | 215 MPa / 31,183 psi | 190 MPa / 27,557 psi | 1 |
VAAK GESTELD VRAGEN
WAT IS HET VERSCHIL TUSSEN 3003 H14 VS 3105 H24? WAT ZIJN DE SPECIFICATIES VAN 3105 H24 ALUMINIUM% 3f WAT ZIJN DE SPECIFICATIES VAN 3105 H14 ALUMINIUM% 3f WAT IS 3105 GESCHILDERD ALUMINIUM BLAD?
Wat is het verschil tussen 3003 H14 vs 3105 H24?
ANTWOORD:
There are a couple differences between 3003 H14 and 3105 H24. One of them is the Brinell Hardness; 3003 H14 has 42 BHN and 3105 H24 has 47 BHN. Another difference is the Fatigue Strength; 3003 H14 has only 60 MPa, whereas 3105 H24 has 74 MPa. In the alloy composition, 3003 H14 contains more Magnesium than 3105 H24. But 3105 H24 contains a little bit of Titanium, Chromium and Copper that 3003 H14 does not have.